產(chǎn)品詳情
瑞典伊薩E71T-1碳鋼藥芯焊絲
Dual Shield Arc 71焊絲伊薩低碳鋼藥芯焊絲E71T-1焊絲
|
種類 |
焊材牌號(hào) |
規(guī)格 |
包裝 |
分類等級(jí) |
|
低碳鋼 |
OK AristoRod 12.50 |
0.8~1.6 |
18Kg |
AWS A5.18 ER70S-6 |
|
OK AristoRod 12.57 |
0.8~1.6 |
18Kg |
AWS A5.18 ER70S-3 |
|
|
OK AristoRod 12.62 |
0.8~1.6 |
18Kg |
AWS A5.18 ER70S-2 |
|
|
OK AristoRod 12.63 |
0.8~1.6 |
18Kg |
AWS A5.18 ER70S-6 |
|
|
OK AristoRod 12.65 |
0.8~1.6 |
18Kg |
AWS A5.18 ER70S-6 |
|
|
高強(qiáng)度鋼 |
OK AristoRod 13.08 |
0.8~1.6 |
18Kg |
AWS A5.28 ER80S-D2 |
|
OK AristoRod 13.09 |
0.8~1.6 |
18Kg |
AWS A5.28 ER80S-G |
|
|
OK AristoRod 13.12 |
0.8~1.6 |
18kg |
AWS A5.28 ER80S-G |
|
|
OK AristoRod 13.13 |
0.8~1.6 |
18Kg |
AWS A5.28 ER100S-G |
|
|
OK AristoRod 13.22 |
0.8~1.6 |
18kg |
AWS A5.28 ER90S-G |
|
|
OK AristoRod 13.26 |
0.8~1.6 |
18Kg |
AWS A5.28 ER80S-G |
|
|
OK AristoRod 13.29 |
0.8~1.6 |
18kg |
AWS A5.28 ER100S-G |
YD127普通錳型堆焊藥芯焊絲
說(shuō)明：PK－YD127是低氫型渣系的堆焊藥芯焊絲，采用直流反接。該焊絲通過(guò)錳元素提高堆焊合金的硬度，由于加入合金元素少，經(jīng)濟(jì)性高，較適合于輕微磨損機(jī)件。
用途：用于堆焊受磨損的中、低碳鋼或低合金鋼的表面，如車軸、齒輪、攪拌機(jī)葉片、行走主動(dòng)輪等。
堆焊金屬主要成分（％）
|
C |
Mn |
|
≤0.20 |
≤4.20 |
堆焊層硬度：HRC≥30
參考規(guī)范：
|
焊絲直徑（ｍｍ） |
焊接電流（A） |
焊接電壓（V） |
|
φ1.6 |
220-320 |
25-32 |
|
φ2.0 |
250-350 |
27-34 |
YD256高錳鋼堆焊藥芯焊絲
說(shuō)明：PK－YD256是金屬粉型高錳鋼堆焊藥芯焊絲，采用直流反接。該焊絲堆焊時(shí)電弧穩(wěn)定，飛濺小，焊縫成型美觀。堆焊建議使用小電流，窄道焊，趁紅熱時(shí)立即錘擊或水淬，以減小裂紋傾向。堆焊金屬為奧氏體高錳鋼，具有加工硬化耐磨的特點(diǎn)
用途：適用于各種破碎機(jī)、高錳鋼軌、推土機(jī)等受沖擊而易磨損部分的堆焊。
堆焊金屬主要成分（％）
|
C |
Mn |
Si |
其它元素總量 |
|
≤1.10 |
11.0-16.0 |
≤1.30 |
≤5.00 |
堆焊層硬度：HB≥170
參考規(guī)范：
|
焊絲直徑 |
焊接電流 |
焊接電壓 |
CO2氣體流量（L/min） |
|
φ1.2 |
160-260 |
24-30 |
15-20 |
|
φ1.6 |
220-320 |
26-32 |
15-25 |